Kinetics of Solid-State Reactive Diffusion between Au and Al

Minho O and Masanori Kajihara

Department of Materials Science and Engineering, Tokyo Institute of Technology, Yokohama 226-8502, Japan

In the wire bonding technique, a thin Au wire is interconnected with an Al layer on a Si chip. During energization heating at solid-state temperatures, however, brittle Au-Al compounds with high electrical resistivities are formed at the interconnection by the reactive diffusion between Au and Al. In order to examine the growth behavior of the Au-Al compounds, the kinetics of the reactive diffusion was experimentally observed using sandwich Al/Au/Al diffusion couples. The diffusion couple was prepared by a diffusion bonding technique and then isothermally annealed at temperatures of 623–723 K for various times up to 103 h. Under such annealing conditions, the diffusion couple is practically considered semi-infinite. Owing to annealing, compound layers consisting of AuAl2, AuAl and Au8Al3 are produced at the initial Au/Al interface in the diffusion couple. The volume fraction in the compound layers is larger for Au8Al3 than for AuAl and AuAl2 in the early stages but becomes smaller for Au8Al3 than for AuAl and AuAl2 in the late stages. However, there are no systematic dependencies of the volume fraction on the annealing time and temperature. The total thickness of the compound layers is proportional to a power function of the annealing time. The exponent of the power function is smaller than 0.5 at 673–723 K. The exponent smaller than 0.5 means that the interdiffusion across the compound layers governs the layer growth and boundary diffusion predominantly contributes to the interdiffusion. On the other hand, at 623 K, the exponent is equal to unity for annealing times shorter than 8 h but smaller than 0.5 for those longer than 8 h. The exponent of unity indicates that the layer growth is controlled by the interface reaction at the migrating interface. Thus, at T = 623 K, the transition of the rate-controlling process occurs at a critical annealing time of 8 h.

(Received 2010/12/24; Accepted 2011/1/20; Published 2011/3/2)

Keywords: reactive diffusion, intermetallic compounds, interface reaction, gold-aluminum system

PDF(Free)PDF (Free) Table of ContentsTable of Contents

REFERENCES

  1. L. Bernstein: Semicond. Prod. August (1961) 35–39.
  2. B. Selikson and T. A. Longo: Proc. IEEE 52 (1964) 1638–1642.
  3. J. A. Cunningham: Solid-St. Electron. 8 (1965) 735–745.
  4. I. A. Blech and H. Sello: J. Electrochem. Soc. 113 (1966) 1052–1054.
  5. G. V. Browning, L. E. Colteryahn and D. G. Cummings: Physics of Failure in Electronics, vol.4, (RADC, 1964) p.428.
  6. E. Philofsky: Solid-St. Electron. 13 (1970) 1391–1399.
  7. G. Majni, C. Nobili, G. Ottaviani and M. Costato: J. Appl. Phys. 52 (1981) 4047–4054.
  8. H.-S. Chang, J. X. Pon, K.-C. Hsieh and C. C. Chen: J. Electron. Mater. 30 (2001) 1171–1177.
  9. N. J. Noolu, N. M. Murdeshwar, K. J. Ely, J. C. Lippold and W. A. Baeslack III: Metall. Mater. Trans. A 35A (2004) 1273–1280.
  10. N. Noolu, N. Murdeshwar, K. Ely, J. Lippold and W. Baeslack III: J. Electron. Mater. 33 (2004) 340–352.
  11. C. D. Breach and F. Wulff: Microelectr. Reliab. 44 (2004) 973–981.
  12. A. Karpel, G. Gur, Z. Atzmon and W. D. Kaplan: J. Mater. Sci. 42 (2007) 2347–2357.
  13. C. D. Breach and F. W. Wulff: Gold Bull. 42 (2009) 92–104.
  14. T. B. Massalski, H. Okamoto, P. R. Subramanian and L. Kacprzak: Binary Alloy Phase Diagrams, vol.1, (ASM International, Materials Park, Ohio, 1990) p.122.
  15. H. Okamoto: J. Phase Equil. Dif. 26 (2005) 391–393.
  16. Y. Tejima, S. Nakamura and M. Kajihara: J. Mater. Sci. 45 (2010) 919–928.
  17. P. G. Shewmon: Diffusion in Solids, (McGraw-Hill Book Company, New York, 1963) pp.12–122.
  18. Metals Data Book, ed. by Japan Inst. Metals, (Maruzen, Tokyo, 1993) p.20.
  19. A. Furuto and M. Kajihara: Mater. Trans. 49 (2008) 294–303.
  20. Y. L. Corcoran, A. H. King, N. de Lanerolle and B. Kim: J. Electron. Mater. 19 (1990) 1177–1183.
  21. R. Pretorius, A. M. Vredenberg and F. W. Saris: J. Appl. Phys. 70 (1991) 3636–3646.
  22. F. Togashi and T. Nishizawa: J. Japan Inst. Metals 40 (1976) 12–21.
  23. M. Kajihara: J. Mater. Sci. 44 (2009) 2109–2118.
  24. M. Kajihara: Acta Mater. 52 (2004) 1193–1200.


[JIM HOME] [JOURNAL ARCHIVES]

© 2011 The Japan Institute of Metals
Comments to us : editjt@jim.or.jp