Nanoscopic Strength Analysis of Work-Hardened Low Carbon Austenitic Stainless Steel, 316SS

Nobuo Nagashima and Saburo Matsuoka

Materials Information Technology Station, National Institute for Materials Science (MITS/NIMS), Tsukuba 305-0047

Abstract:

Stress corrosion cracking (SCC) occurs in shrouds and piping of low carbon austenitic stainless steels at nuclear power plants. A work-hardened layer, where the transgranular SCC initiates, is considered to be one of the probable cause for this occurrence. In order to clarify the microstructural characteristics of work-hardened layer at the surface of shrouds or piping, the strengthen analysis of low carbon austenitic stainless steel, 316SS, rolled at the reduction in area, RA, of 10, 20, 30, 40 and 50% at room temperature were conducted on a nanoscopic scale, using an ultra-microhardness tester, TEM and SEM. TEM and SEM observation showed that the microstructural parameters are the dislocation cell size, dcel, coarse slip spacing, lcsl, and austenitic grain size, dγ. Referring 10dcel and 10lcsl, Vickers hardness, HV, corresponding to macro strength was expressed as Hv=Hvbas*+Hvsol*+Hvdis*+Hvcel*+Hvcsl*. Hvbas* (= 100) is the base hardness, Hvsol* is the solid solution strengthening hardness, Hvdis* is the dislocation strengthening hardness in the dislocation cell, and Hvcel* and Hvcsl* are the fine grain strengthening hardness due to the dislocation cell and coarse slip. Hvsol* was about 50, independently of RA. Hvdis* was zero at RA<30% and increased at RA>30%. Hvcel* and Hvcsl* increased with increasing in RA and were kept constant at about 50 and 120 at RA=20 and 30%, respectively. It was suggested from these results that all dislocations introduced by rolling might be dissipated for the creation of dislocation cells and coarse slips at RA<30% and that the microstructure contributing to the fine grain strengthening due to the dislocation cell and coarse slip might be accomplished at RA=30%. The dislocation strengthening in the dislocation cell might begin to operate at RA>30%.


(Received 2004/11/12)

Keywords:

BWR (Boiling Water Reactor), SCC (Stress Corrosion Cracking), low carbon austenitic stainless steel, 316SS, work hardening, nanoindentation, microstructural parameters


PDF(Free)PDF (Free)     Table of ContentsTable of Contents

Please do not copy without permission.